1, danniya taimako kafin plating inda iyakar tensile ƙarfi ya fi 1034Mpa key da muhimmanci sassa kafin plating ya kamata a 200 ± 10 ℃ danniya taimako na fiye da 1 hours, carburizing ko surface quenching sassa ya zama a 140 ± 10 ℃ danniya taimako. fiye da 5 hours.
2. Maganin tsaftacewa da aka yi amfani da shi don tsaftacewa bai kamata ya yi tasiri a kan ƙarfin dauri na sutura ba kuma babu lalata akan matrix.
3. Acid kunnawa acid kunna bayani bayani ya kamata a iya cire lalata kayayyakin da oxide fim (fata) a saman sassa, ba tare da wuce kima lalata a kan matrix.
4, galvanized za a iya amfani da zincategalvanizedko chloride galvanized tsari, ya kamata amfani da dacewa Additives saduwa da bukatun wannan ma'auni shafi.
5, bayan da haske plating ya kamata a za'ayi haske magani.
6, passivation don cire hydrogen sassa ya zama passivation bayan kau da hydrogen, passivation kafin aikace-aikace na 1% H2SO4 ko 1% hydrochloric acid kunnawa 5 ~ 15s.Passivation za a bi da tare da launi chromate sai dai in ba haka ba a cikin zanen zane.